Chemical Composition
| Alloy
EN
Chemical
Composition |
|
|
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
NI |
Zn |
Ga |
V |
Ti |
Each |
Total |
6005A |
Al
SiMg(A) |
0.5-0.9 |
0.35 |
0.30 |
0.50 |
0.4-0.7 |
0.30
|
- |
0.20 |
- |
- |
0.10 |
0.05
|
0.15
|
6060 |
Al
MgSi |
0.3.-0.6 |
0.1.0.3 |
0.10 |
0.10 |
0.35-0.6 |
0.05 |
- |
0.15 |
- |
- |
0.10 |
0.05
|
0.15
|
6061 |
Al
Mg1SiCu |
0.4.0.8 |
0.70 |
0.15.0.4 |
0.15 |
0.8-1.2 |
0.04.0.35 |
- |
0.25 |
- |
- |
0.15
|
0.05
|
0.15
|
6063 |
Al
Mg0.7Si |
0.2.0.6 |
0.35 |
0.10 |
0.10 |
0.45-0.9 |
0.10
|
- |
0.10 |
- |
- |
0.10 |
0.05
|
0.15
|
Mechanical
Properties
| Alloy
6005 (Al SiMg)
Mechanical
Properties
|
Temper |
Dimensions |
Rm |
|
Rp0.2 |
|
A |
A
50mm |
| |
mm |
MPA |
|
MPA |
|
% |
% |
Open
Profile |
wall
thickness (e) |
min. |
max. |
min. |
max |
min. |
min. |
T4
* |
≤
25 |
180 |
|
90 |
|
15 |
13 |
| |
≤
5 |
270 |
|
225 |
|
8 |
6 |
| |
5
< e ≤ 10 |
260 |
|
215 |
|
8 |
6 |
| |
10
< e ≤ 25 |
250 |
|
200 |
|
8 |
6 |
Hollow
Profile |
3<
e ≤ 25 |
|
|
|
|
|
|
T4
* |
≤10 |
180 |
|
90 |
|
8 |
6 |
T6
* |
≤
5 |
255 |
|
215 |
|
8 |
6 |
| |
5
< e ≤ 15 |
250 |
|
200 |
|
8 |
6 |
| * Properties
that may be obtained by press quenching |
| Alloy
6060 (Al MgSi)
Mechanical
Properties
|
Temper |
Dimensions |
Rm |
|
Rp0.2 |
|
A |
A
50mm |
| |
mm |
MPA |
|
MPA |
|
% |
% |
Open
Profile |
wall
thickness (e) |
min. |
max. |
min. |
max |
min. |
min. |
T4
* |
≤
25 |
120 |
|
60 |
|
16 |
14 |
T5
* |
≤ 3 |
160 |
|
120 |
|
8 |
6 |
| |
5<
e ≤ 25 |
140 |
|
100 |
|
8 |
5 |
T6
* |
≤10 |
190 |
|
150 |
|
8 |
6 |
| |
3<
e ≤ 25 |
170 |
|
140 |
|
8 |
6 |
T66
* |
≤10 |
215 |
|
160 |
|
8 |
6 |
| |
3<
e ≤ 25 |
195 |
|
150 |
|
8 |
6 |
| * Properties
that may be obtained by press quenching |
| Alloy
6061 (Al
Mg1SiCu)
Mechanical
Properties |
Alloy
6061 |
Dimensions |
|
|
|
|
|
|
Temper |
mm |
Rm |
|
Rp0.2 |
|
A |
A
50mm |
| |
wall
thickness (e) |
MPA |
|
MPA |
|
% |
% |
| |
≤ 25 |
min. |
max. |
min. |
max. |
min. |
min. |
T4
* |
≤
5 |
180 |
|
110 |
|
15 |
13 |
T6
* |
5
< e ≤ 25 |
260 |
|
240 |
|
9 |
7 |
| |
|
260 |
|
240 |
|
10 |
8 |
| * Properties
that may be obtained by press quenching |
| Alloy
6063 (Al Mg0.7Si)
Mechanical
Properties |
Temper |
Dimensions |
Rm |
|
Rp0.2 |
|
A |
A
50mm |
| |
mm |
MPA |
|
MPA |
|
% |
% |
Open
Profile |
wall
thickness (e) |
min. |
max. |
min. |
max |
min. |
min. |
T4
* |
≤
25 |
130 |
|
65 |
|
14 |
12 |
T5
* |
≤ 3 |
175 |
|
130 |
|
8 |
6 |
| |
3 <
e ≤ 25 |
160 |
|
110 |
|
7 |
5 |
T6
* |
≤10 |
215 |
|
170 |
|
8 |
6 |
| |
10
< e ≤ 25 |
195 |
|
160 |
|
8 |
6 |
T66
* |
≤ 10 |
245 |
|
200 |
|
8 |
6 |
| |
10
< e ≤ 25 |
225 |
|
180 |
|
8 |
6 |
| * Properties
that may be obtained by press quenching |
| |